Showing 3 results for Setting
Evaluation of the physical properties of the Iranian temporary cement, Tem Band, and the foreign one, Temp Bond, compared to ISO 3107
V. Soltan Karimy , Sm. Bayanzadeh ,
Volume 19, Issue 3 (6-2006)
Abstract

Background and Aim: Iranian temporary cement, Tem Band, has been manufactured by Golchai company, and introduced to market as a suitable material but its properties have not been tested yet. The aim of this study was to investigate the setting time, film thickness, compressive strength, disintegration and arsenic content of Tem Band and Temp bond temporary cements and compare them to ISO 3107. Materials and Methods: In this experimental study, 12 samples from each cement were obtained and setting time, film thickness, compressive strength, solubility and disintegration were tested according to ISO 3107. In addition, arsenic content was tested based on ASTM 6052. Data were analyzed with t-test and p<0.05 was considered as the limit of significance.

Results: The average setting time of Tem Band was 5 minutes and 47 seconds (4.17 minutes for Temp Bond), the average film thickness was 6.67 micrometer for Tem Band and 4.08 micrometer for Temp Bond. There was no difference between two cements regarding setting time and film thickness and for both was at the standard range. Compressive strength of Tem Band was 5.67 MPa and 8.5 MPa for Temp Bond. The difference was statistically significant but for both cements was less than standard (35 MPa). There was no significant difference regarding the solubility and disintegration tests. In both samples, the solubility and disintegration values were in standard ranges. Both cements did not contain arsenic but lead level was at the maximum standard range in Tem Band.

Conclusion: Considering these results, both cements are applicable to different clinical situations based on their physical properties. Studies on the biocompatibility of the Iranian cement is recommended.


Comparison of some properties of four provisional restorations resin: Trim, Tempron, Acropars TRII & Duralay (Aria Dent)
A. Monzavi , S. Zarati , T. Jafarzadeh , Mh. Amini ,
Volume 19, Issue 3 (6-2006)
Abstract

Background and Aim: Use of provisional restorations is one of the important phases in the treatment of patients who need fixed prosthesis. Some physical properties are required for these materials. The purpose of this study was the comparison of some physical properties of 4 kinds of resins: Trim, Tempron, Duralay (Aria Dent) and Acropars TRII.

Materials and Methods: In this experimental study, transverse-strength (TS), setting time (ST), polymerization shrinkage (PS) and temperature rise (TR) during polymerization were tested. In transverse strength test, 5 samples of each resin were made. TS testing was done with an Instron testing machine. ST testing (5 samples in each group) was done with Gilmore needle. In PS test, 11 cylindric samples were prepared from each resin and the shrinkage was examined with digital micrometer (up to 24 hours). In TR test, after mixing the powder and liquid of resins (8 samples in each group), the temperature rise was recorded with 10 seconds interval (up to 15 minutes). Data were analyzed with one-way ANOVA and Tukey HSD tests with p<0.05 as the limit of significance.

Results: In TS test, all samples of Trim were bent and no fracture was observed, while Tempron and Duralay showed no significant difference. Both Tempron and Duralay revealed high significant difference with Acropars TRII (P <0.01). In ST test, the difference between groups was significant (P<0.01). The lowest ST was observed in Acropars TRII (7 min), and the highest in Tempron (9.53 min). In PS test, significant difference was observed between Trim and Acropars TRII (P<0.01). PS was completed after 120 min in Tempron and Trim groups. However, PS continued to increase in other groups. In TR test, the difference between groups was significant (P<0.05). Duralay showed the highest TR and the lowest was seen in Trim.

Conclusion: In this study, Trim showed better properties than other studied groups. Acropars TRII had the lowest strength. The highest temperature rise was recorded for Duralay and Tempron, respectively.


Comparison of setting time of an Iranian MTA with a foreign MTA
Sakineh Arami, Sakineh Arami, Masoumeh Hasani Tabatabaei, Seyed Reza Najafzadeh, Ahmadreza Shamshiri, Zohreh Moradi,
Volume 30, Issue 4 (1-2018)
Abstract
Background and Aims: According to many uses of MTA in different treatments, studying about its properties like the setting time, is of great importance. The aim of this study was to compare the initial and final setting time of an Iranian MTA and a foreign MTA.
Materials and Methods: Seven samples were in each group; for measurement of initial and final setting time of MTAs, a mold with dimension of 2×10 mm was prepared. The cements after mixation were put into an incubator with temperature of 37ₒC and humidity of 90%. After mixing of cements, a Gilmore needle with a weight of 100 gr and active tip of 2 mm was used vertically on the surface of MTA for measurement of the initial setting time. Setting was measured by the start of cement mixation to the time the tip of the needle didn’t penetrate to the surface of MTA. For measurement of the final setting time a Gilmore needle with a weight of 456 gr and active tip of 1mm was used vertically on the surface of MTA. The ANOVA test followed by Tukey test was used for comparison of the mean setting time between an Iranian and foreign MTA. The statistical difference was considered significant at the level of 0.05.
Resultes: The mean initial setting time Angelus and Root MTAs were 13.57±0.91 and 11.14±0.92 min, the mean final setting of Angelus and Root MTA, were 48.93±1.54 and 37.86±1.5 min while the initial setting time of Angelus MTA lasted for 0.53±43.2 more min than Root MTA (P=0.001). The final setting time of Angelus MTA took longer for 110.7±0.82 min than Root MTA (P=0.001).
Conclusion: The initial and final setting time of the Iranian MTA was shorter than the foreign one and thus it could a more alternative option in this respect.