Journal of Dental Medicine

Background and Aim: Considering flexural strength of fiber-reinforced composites (FRC) and also the role of conservative cavities in protecting sound tissue of abutments, the aim of this study was to evaluate the fracture resistance of these bridges by handmade samples in vitro.

Materials and Methods: In this experimental in vitro study, 44 sound newly extracted teeth were used to make 22 fixed inlay bridges including 11 three unit anterior upper inlay bridges substituting clinical model of upper central and 11 three unit posterior lower inlay bridges substituting clinical model of lower first molar. Specimens were prepared with FRC and mounted with artificial PDL in acryl. Cases were exposed to final load by using Universal Testing Machine (Instron 1195) with the speed of 1 mm/min. Statistical analysis was performed by Kolmogorov- Smirnov, independent sample T and Kaplan-Meier tests with p<0.05 as the level of significance.

Results: Based on the statistical tests, the 95% confidence interval of mean was 450-562 N in anterior and  1473- 1761 N in posterior area. Fracture strength was high in the studied groups. Fractures in both groups occurred on composite facing, and the framework remained intact. The highest percentage of fracture in posterior teeth was in the middle of pontic towards the distal connector and in the anterior teeth in the lateral connector, between central pontic and lateral abutment. Using the independent sample T  test a significant statistical difference was observed between two groups (P<0.001). The fracture resistance of anterior samples was lower than the posterior ones.

Conclusion: Based on the results of this study regarding the high fracture resistance in both areas FRC inlay bridges could be recommended for upper anterior and lower posterior teeth in clinical dentistry certainly more studies are needed to ascertain this treatment option.